It is shown that neither of two controversial interpretations of recovery data obtained after a low temperature irradiation with high energy particles on silver - zinc - alloys in two laboratories is correct and that instead a third interpretation based on results of measurements of radiation enhanced diffusion and quenching leads to the conclusion that in these alloys, only vacancies are able to increase the degree of order and that interstitials are only slightly less mobile than vacancies.