BULK MODULI AND HIGH-PRESSURE PHASES OF THE URANIUM ROCKSALT STRUCTURE COMPOUNDS - II. THE MONOPNICTIDES
The high-pressure crystal structures of the compounds UX, where X = N, P, As and Sb are studied using X-ray diffraction in the pressure range up to about 60 GPa. Rhombohedral distortions are observed for UN and UP above 29 GPa and 10 GPa, respectively. In UP a further transformation to an orthorhombic phase occurs at 28 GPa. UAs and USb transform to the CsCl structure at 20 GPa and 9 GPa, respectively. The latter transformations show a considerable hysteresis when the pressure is released. The scaling behaviour of the bulk modulus is studied. It is confirmed that a log-log plot of bulk modulus versus specific volume for the cubic phases gives a straight line with a slope near -5/3.
Bibliographic Reference: ARTICLE: HIGH PRESSURE RESEARCH, VOL. 1 (1989) PP. 253-266