Abstract

Fuel restructuring, the redistribution of Pu and the behaviour of Xe and Cs have been investigated in three segments of MOX fuel. Two of the segments had been irradiated under normal conditions to burn-ups of 23.2 and 38.8 GWd t; the third had been transient-tested to 42 kW m, for 52.2 h at 26.2 GWd t. The fuel was fabricated by the AUPuC process, which involved mechanically blending a master-mix of 70 30 UO(2)-PuO(2) with natural UO(2) powder. The product contained nominally 3.2 wt% Pu and consisted of agglomerates of master-mix particles less than 100 microns in size, irregularly dispersed in a matrix of UO(2). The local concentrations of Pu, Xe and Cs were determined by electron probe microanalysis (EPMA). The volume fraction of pores and large bubbles in the MOX agglomerates and UO(2) matrix was measured using a Leitz quantitative image analyser, connected to a Reichert Telatom 62 optical microscope.

Additional information

Authors: WALKER C T, JRC KARLSRUHE ESTAB. (DE);COQUERELLE M JRC KARLSRUHE ESTAB. (DE), JRC KARLSRUHE ESTAB. (DE)
Bibliographic Reference: PAPER PRESENTED: JAHRESTAGUNG KERNTECHNIK 1990, NUERNBERG (DE), MAY 15-17, 1990 AVAILABLE FROM COMMISSION OF THE EUROPEAN COMMUNITIES, DG XIII-C-3, L-2920 LUXEMBOURG AS PAPER EN 35242 ORA
Availability: Can be ordered online
Record Number: 1989128087200 / Last updated on: 1990-11-01
Category: PUBLICATION
Original language: EN
Available languages: en
Follow us on: RSS Facebook Twitter YouTube Managed by the EU Publications Office Top