The effect of niobium on the oxidation behaviour of titanium in N2/20% 02 atmospheres

Funded under: FP5


A systematic study on the isothermal oxidation of Ti-based materials, i.e. pure Ti, Ti-4at.%Nb, and niobium implanted Ti, was conducted in order to obtain more insight into the role of small amounts of niobium on the oxidation of niobium-containing intermetallic alloys. Examinations were performed by thermogravimetry and by studying the surface morphology, structure and composition of the oxidation products. Hardness measurements were made to quantify the amount of dissolved oxygen in the metallic matrix. Oxidation experiments performed in dry and humidified nitrogen/oxygen atmospheres at 800 degrees Celsius showed that the presence of niobium not only significantly reduced the growth of titania, but also significantly reduced the influence of water on the oxidation behaviour of Ti. This beneficial effect was explained by the formation of a continuous nitride layer, already during the initial stage of the oxidation, at the scale/substrate interface, induced by the presence of small amounts of niobium.

Additional information

Authors: PEREZ P, European Commission, Joint Research Centre, Ispra (IT);HAANAPPEL V A C, European Commission, Joint Research Centre, Ispra (IT);STROOSNIJDER M F, European Commission, Joint Research Centre, Ispra (IT)
Bibliographic Reference: Article: Materials Sciences and Engineering, A284 (2000) pp. 126-137
Availability: Materials Sciences and Engineering (Journal)
Record Number: 200012783 / Last updated on: 2000-09-20
Original language: en
Available languages: en
Follow us on: RSS Facebook Twitter YouTube Managed by the EU Publications Office Top