Cel Longitudinal surface cracking and depressions in continuously cast, medium carbon and austenitic stainless steels remain a problem, particularly for small cracks located near the slab mid-faces or close to the edges. The aim of the study is to develop mould technologies which will reduce the initial formation of longitudinal defects in steady state casting conditions and also to assess the effects of transient conditions on crack formation using neural network technology. The conditions immediately below the mould and in the top zone which influence crack propagation will also be investigated. The study will add to the fundamental knowledge of longitudinal defect formation and enable the identification of high performance casting conditions; this will also assist development of near net shape casting. Program(-y) ECSC-STEELRES 8C - Medium-term guidelines (ECSC) for the programmes of technical steel research and of steel pilot/demonstration projects, 1991-1995 Temat(-y) C3 - Casting and solidification Zaproszenie do składania wniosków Data not available System finansowania CSC - Cost-sharing contracts Koordynator British Steel plc Wkład UE Brak danych Adres TS6 6UB Middlesbrough Zjednoczone Królestwo Zobacz na mapie Koszt całkowity Brak danych Uczestnicy (2) Sortuj alfabetycznie Sortuj według wkładu UE Rozwiń wszystko Zwiń wszystko CENTRO SVILUPPO MATERIALI SPA Włochy Wkład UE Brak danych Adres Via di Castel Romano 100/102 00128 ROMA EUR Zobacz na mapie Koszt całkowity Brak danych INSTITUT DE RECHERCHES DE LA SIDERURGIE FRANÇAISE Francja Wkład UE Brak danych Adres Voie Romaine - BP 320 57214 MAIZIERES-LES-METZ CEDEX Zobacz na mapie Koszt całkowity Brak danych