Cel IT IS KNOWN THAT THE RESISTANCE OF METALS TO ABRASIVE WEAR IS DEPENDENT NOT ONLY ON MACROHARDNESS BUT ALSO ON MICROSTRUCTURAL PARAMETERS OF THE MATERIAL SUCH AS MICROSTRUCTURAL HOMOGENEITY AND HETEROGENEITY, DISTRIBUTION OF HARD PHASES, TOUGHNESS, BRITTLENESS, ETC. AS A RESULT THERE IS A GROWING INTEREST IN THE USE OF DUAL-PHASE STEELS SINCE THEY POSSESS THOUGHNESS AND THE MECHANICAL STRENGTH IN A PARTICULARLY SATISFACTORY COMBINATION. IN PARTICULAR EXTENSIVE RESEARCH ACTIVITIES HAVE BEEN LAUNCHED UNDER THE AUSPICES OF THE ECSC WITH THE AIM OF DEVELOPING HIGH-CARBON DUAL-PHASE STEELS. MARKET RESEARCH, HOWEVER, SHOWS THAT THERE IS AT PRESENT A STRONG DEMAND FOR STEEL PLATE (ESPECIALLY LIGHT PLATE) POSSESSING HIGH WEAR RESISTANCE AND, IN ADDITION, SATISFACTORY WELDABILITY AND PLIABILITY. FOR THESE REASONS IT IS ESSENTIAL TO ARRANGE FOR A PROGRAMME OF RESEARCH INTO THE POSSIBILITY OF DEVELOPING DUAL-PHASE STEELS WITH A MAXIMUM CARBON CONTENT OF 0.3 % WHICH POSSESS THE ABOVE MENTIONED PROPERTIES IN THE MOST SUITABLE COMBINATION. Program(-y) ECSC-STEELRES 6C - Medium-term orientation (ECSC) "steel research in relation to the General Objectives for Steel", 1981-1985 Temat(-y) Data not available Zaproszenie do składania wniosków Data not available System finansowania Data not available Koordynator MATERIALS RESEARCH CENTRE Wkład UE Brak danych Adres Via di Castel Romano 100/102 00128 ROMA Włochy Zobacz na mapie Koszt całkowity Brak danych