Objectif Rail steel are designed to resist wear and rolling contact fatigue caused by forces transmitted through the wheel/rail contact zone. The aims of the project are twofold: to investigate morphology, transformation characteristics and properties of bainite mixed with a low amount of lath martensite, as compared to conventional pearlite structure, and to define chemical compositions, for given hot rolling and in line/off line cooling conditions to achieve the optimum bainitic structure able to develop hardness values higher than 400 HB minimum tensile strength of 1400 MPa, good wear resistance and elongation = 10%. The welding behaviour will also be studied. Programme(s) ECSC-STEEL C - Medium-term guidelines for the ECSC steel RTD programme of research and pilot/demonstration projects, 1996-2002 Thème(s) D3 - Physical metallurgy of rolling and finishing Appel à propositions Data not available Régime de financement CSC - Cost-sharing contracts Coordinateur CENTRO SVILUPPO MATERIALI SPA Contribution de l’UE Aucune donnée Adresse Via di Castel Romano 100/102 00128 ROMA EUR Italie Voir sur la carte Coût total Aucune donnée Participants (2) Trier par ordre alphabétique Trier par contribution de l’UE Tout développer Tout réduire CENTRE DE RECHERCHES METALLURGIQUES Belgique Contribution de l’UE Aucune donnée Adresse Rue Ernest Solvay, 11 4000 LIEGE Voir sur la carte Coût total Aucune donnée VOEST ALPINE SCHIENEN Autriche Contribution de l’UE Aucune donnée Adresse Kerpely Strasse 199 8700 LEOBEN Voir sur la carte Coût total Aucune donnée