Valorization of undervalued recycled polyethylene terephthalate (rPET) by supercritical CO2-assisted extrusion foaming CO2-assisted extrusion

Información del proyecto

R-PETFOAM

Identificador del acuerdo de subvención: 101148945

DOI

10.3030/101148945

Proyecto cerrado

Fecha de la firma de la CE 24 Abril 2024

Fecha de inicio 2 Septiembre 2024

Fecha de finalización 1 Marzo 2026

Financiado con arreglo a

• Marie Skłodowska-Curie Actions (MSCA)

Coste total

Sin datos

Aportación de la UE

€ 135 864,72

Coordinado por

FUNDACION CIDAUT
Spain

Periodic Reporting for period 1 - R-PETFOAM (Valorization of undervalued recycled polyethylene terephthalate (rPET) by supercritical CO2-assistedextrusion foaming CO2-assisted extrusion)

Período documentado: 2024-09-02 hasta 2026-03-01

Resumen del contexto y de los objetivos generales del proyecto

Plastics have fundamentally improved modern living, yet their short life cycle and the sheer volume of resulting waste have triggered a global environmental crisis. Polyethylene terephthalate (PET) is the most widely used plastic for beverage packaging. While clear PET bottles are successfully mechanically recycled back into new bottles, the same cannot be said for mixed-color, or opaque PET streams. Because these colored plastics have high compositional variation and lower aesthetic appeal, they suffer from low industrial demand. Consequently, this "orphan" waste stream is frequently downcycled into fibers, sent to landfills, or incinerated, breaking the loop of the circular economy.

The R-PETFOAM project was born to solve this exact problem. The overall objective was to upcycle these undervalued, mixed-color PET waste streams into high-performance, high-value structural foams. Polymeric foams are lightweight, rigid materials filled with tiny gas bubbles, widely used as the structural core in wind turbine blades, aerospace components, as well as construction and automotive panels. Because foams are inherently opaque, the variable color of the plastic waste become completely irrelevant.

The project's pathway to impact relies on replacing toxic, highly polluting, or expensive virgin core materials (like PVC or virgin PET foams) with a 100% recycled alternative, processed using an eco-friendly blowing agent: supercritical carbon dioxide (scCO2). By demonstrating that mixed-color waste can be transformed into a premium engineering material, R-PETFOAM aims to create a lucrative market pull. Valorizing just a fraction of Europe’s undervalued colored PET waste could generate millions in revenue while drastically reducing the carbon footprint of both the waste management and composite manufacturing sectors.

Trabajo realizado desde el comienzo del proyecto hasta el final del período abarcado por el informe y los principales resultados hasta la fecha

To turn degraded, mixed-color plastic waste into a robust foam, a major technical hurdle had to be overcome: recycled PET loses its "melt strength" during its life cycle. When melted, it flows like water, making it impossible to trap expanding gas bubbles without them collapsing.
1. Restoring the Plastic’s Architecture:
The project team conducted an exhaustive screening of chemical additives known as "chain extenders" (molecules that act like bridges to reconnect broken plastic chains). The main achievement in this phase was the discovery of a "topological synergy." By combining two different types of extenders (one that linearly lengthens the chains, and another that creates hyper-branched, web-like connections), the researchers successfully restored the required melt strength without causing the plastic to harden or clog the machinery.
2. Developing the Green Foaming Process:
The team successfully retrofitted a pilot-scale, continuous twin-screw extruder machine to handle this complex recycled material. They integrated a high-pressure pumping system to inject supercritical CO2 directly into the molten plastic. As the plastic exits the machine, the CO2 expands, creating a foam structure with a high number of trapped bubbles.
3. Turning "Contamination" into a Feature:
The most remarkable achievement occurred when foaming the 100% mixed-color waste. The researchers discovered that the residual solid contaminants inherent to colored waste (such as microscopic aluminum particles and pigments) actually aided the process. These tiny particles acted as "seeds" (nucleating agents) around which the gas bubbles could easily form and the plastic could rapidly crystallize. Instead of ruining the product, the contaminants actively reinforced the cell walls of the foam.

Avances que van más allá del estado de la técnica e impacto potencial esperado (incluida la repercusión socioeconómica y las implicaciones sociales más amplias del proyecto hasta la fecha)

The R-PETFOAM project pushed the boundaries of mechanical recycling by achieving the first successful continuous scCO2 foaming of 100% highly contaminated, mixed-color rPET.
The resulting engineered foams achieved metrics successfully rivalling established products and commercial standards of the PET foam industry. The project proved that we can achieve excellent structural performance using the lowest-grade plastic waste.

Extrusion Foaming Final Setup

Extrusion Foaminog progress