Periodic Reporting for period 1 - PROMISES (Properties of nanomaterials made from misfit-layered compounds revealed by electron microscopy and simulations)
Période du rapport: 2021-09-01 au 2023-08-31
MLCs are complex systems which require advanced characterization methods to shed light on their performance in potential applications, a main objective of PROMISES. Therefore, nanotubular structures of MLCs and related materials are investigated by advanced transmission electron microscopy (TEM) for a better understanding of their structure, properties and the synthesis conditions of the material. A special focus is put on in-situ TEM studies, the second main objective, which allow to study (nano)materials under application-relevant conditions with external stimuli such as heat or electrical currents. Technological development of in-situ TEM is necessary to solve the problem of sample preparation and contacting of individual nanomaterials especially for electrical in-situ analysis. An additional issue in TEM of very thin nanomaterials is the little contrast observed under focused conditions. A solution can be physical phase plates, which improve phase contrast of thin objects and the combination of aberration-corrected TEM with such phase plates was investigated.
In the course of the project, several important findings on MLCs and other layered materials have allowed for a deeper understanding of their structure, properties, stability and the processes involved in the synthesis of these materials. Also, a novel preparation method has been developed to allow the in-situ studies of the stability and evolution of individual MLC nanotubes under the application of high electrical currents. As MLC is a promising candidate for thermoelectrical applications, the possibility of thermoelectrical characterization by in-situ TEM has been explored. As a conclusion, the results obtained in PROMISES have significantly improved the understanding of these materials as well as ameliorated and optimized in-situ TEM characterization approaches of nanomaterials beyond the state of the art.
The second part of the work focused on methodological development of TEM. The combination of aberration correction with Zernike phase plates was successfully studied, a very promising technique to enhance contrast and improve interpretability of TEM images of nanomaterials. The main methodological development was focused on in-situ TEM analysis, especially electrical characterization studies. The thermoelectrical characterization of (nano)materials by in-situ TEM was explored. Proof-of-principle experiments show the induction of a thermo-voltage and the general possibility of such analyses. One of the main challenges for in-situ TEM is a clean preparation and contacting of the sample on the in-situ chip, especially for nanomaterials, whose structure has to be preserved throughout the process. A support-based transfer process was elaborated that provides a high reproducibility at minimum damage and contamination of the material. The process was sent as an investigation result to the office of technology transfer. The technique was tested on various different nanomaterials, which subsequently were studied by in-situ TEM. Results have been obtained on the stability of LaS-TaS2 MLC under high electrical currents, which allows to study the breakdown mechanism. This breakdown mechanism differs largely between materials as have shown similar experiments on carbon-based materials.
In addition to the publication of 6 scientific articles in peer-reviewed journals, the results have been presented at five scientific conferences or seminars. Moreover, several dissemination activities during PROMISES aimed for the non-scientific public, including newspaper articles, the participation at the European Researchers’ Night and the 2021 edition of Science is Wonderful. Worth special mentioning is the creation of a song and movie on Misfit nanotubes published on Youtube.
In the area of methodological development of TEM, progress has clearly gone beyond the state of the art. For the first time, physical Zernike phase plates have been successfully combined with aberration-corrected TEM. The use of phase plates can strongly increase the information content the interpretability of TEM images. The developed support-based sample preparation of individual nanomaterials guarantees high reproducibility with minimum damage and contamination of the materials. This sample preparation method allows, e.g. to study the behavior of materials under high electrical currents by in-situ TEM. Finally, for the first time, studies on thermoelectrical in-situ TEM have been performed, which potentially allows the direct analysis of the interplay between thermoelectrical and structural or chemical properties.
High-performance materials are a key element for sustainable progress in the modern society. The studies performed in the PROMISES project help to understand these materials in a better way.