Objectif
Permanent magnets based on the iron(14)neodymium(2)boron intermetallic compound have been produced by the 4 different techniques sintering, melt spinning, extrusion and mechanical alloying. Due to the deteriorating effects of the microstructure these different techniques have so far led to only 10-20% of the theoretically achievable coercive field. Investigations of magnetisation processes, hysteresis loops, magnetic after effects and domain patterns have been performed on these different materials as a function of temperature and different types of pretreatment. These magnetic measurements have been combined with studies of the microstructure by transmission electron microscopy. In particular, the role of nonmagnetic precipitation, misaligned grains, incompletely magnetically decoupled grains, structure of the intergranular phase have been studied in detail. From a comparison of the different types of permanent magnets a deeper insight into the role of the microstructure with respect to their hard magnetic properties has been obtained. Combining the results of the microstructural and the micromagnetic analysis of the different types of permanent magnets the procedures for optimising the coercive field have been determined.
The above mentioned types of magnets have been prepared with different compositions and additive elements. Melt spun materials have been prepared and analysed in a wide range of preparation parameters. By a well defined optimisation of the microstructure the coercive field of a melt spun iron(72)neodymium(17)boron(7.5)gallium(1.5)niobium magnet could be increased up to 940 kAm{-1} at a temperature of 150 C.
The microstructure of hard magnetic materials was investigated. It was found that:
large coercive fields require a perfect decoupling, an optimal alignment and perfect surfaces of grains;
these conditions can be approached by the combination of production techniques, suitable additives and annealing treatments;
the largest coercive fields are obtained by the melt spinning technique and a composition neodymium 17 iron 72 boron 7.5 gallium 1.5 niobium 2;
magnetic additives increase the coercive field at the expense of remanence, thus decreasing the energy product;
low melting metals such as gallium, aluminium and copper increase the viscosity of the intergranular neodymium rich phase, thus enhancing the magnetic decoupling between the grains;
gallium is more suitable than aluminium and copper because up to 1.4 atomic% gallium is nearly unsoluble in the hard magnetic phase neodymium 2 iron 14 boron while aluminium dissolves in neodymium 2 iron 14 boron where it reduces the remanence;
high melting refractory metals form high melting borides during the sintering process, thus increasing the magnetic decoupling and reducing the corrosivity;
in melt spun magnets the additives niobium, molybdenum and vanadium act as nuclei for a fine dispersed homogeneous grain structure;
the role of the microstructure is described by the microstructural parameters alpha and Neff;
largest alpha values (0.45 to 0.5) are obtained for sintered magnets;
large Neff values (1.2 to 2.0) are found in sintered and mechanically alloyed magnets;
by short time or flash annealing treatments the ideal conditions of a large alpha and a small Neff value can be approached;
the coercive field is nearly independent of the grain size.
The impossibility of approaching the ideal microstructure with alpha of 1 and Neff of 0 is attributed to 4 most effective deteriorating effects:
misaligned grains;
grains coupled by exchange and dipolar interactions;
strong demagnetization fields at sharp edges and corners;
imperfect grain surfaces.
The results detail the role of different microstructures which might help the magnets industry to produce optimally tailored alloys. In particular they clarify the role of magnetic additives, low melting additives and high melting additives in connection with different production techniques allowing the development of desired properties of the hysteresis loop.
Important emerging applications of the work include:
small size, high speed, high efficiency motors and dynamos;
general electrical motors and generators;
medical applications (imaging systems);
new electric cars or starter motors;
efficient, strong and high speed motors for disk drive units;
digital coding, multiflexing, pm digital arrays;
magnetic actuators and sensors;
micromotors, microdevices, magnetic lenses, magnetic confinement and new instrumentation.
Permanent magnets based on the Fe14Nd2B intermetallic compound will be produced by four different techniques : sintering, melt-spinning, extrusion and mechanical alloying. Due to the deteriorating effects of the microstructure these different techniques have so far to only 10-20 % of the theoretically achievable coercive field. Investigations of magnetization processes, hysteresis loops, magnetic after-effects and domain patterns will be performed on these different materials as a function of temperature and different types of pretreatment.
These magnetic measurements will be combined with studies of the microstructure by transmission electron microscopy. In particular, the role of non-magnetic precipitation, misaligned grains, incompletely magnetically decoupled grains, structure of the intergranular phase will be studied in detail. From a comparison of the different types of permanent magnets a deeper insight into the role of the microstructure with respect to their hard magnetic properties will be obtained. Combining the results of the microstructural and the micromagnetic analysis of the different types of permanent magnets the procedures for optimizing the coercive field be determined.
Champ scientifique (EuroSciVoc)
CORDIS classe les projets avec EuroSciVoc, une taxonomie multilingue des domaines scientifiques, grâce à un processus semi-automatique basé sur des techniques TLN. Voir: Le vocabulaire scientifique européen.
CORDIS classe les projets avec EuroSciVoc, une taxonomie multilingue des domaines scientifiques, grâce à un processus semi-automatique basé sur des techniques TLN. Voir: Le vocabulaire scientifique européen.
- sciences agricoles agriculture, sylviculture et pêche agriculture céréales et oléagineux
- sciences naturelles sciences chimiques chimie inorganique métal de transition
- sciences naturelles sciences chimiques chimie inorganique métal pauvre
- ingénierie et technologie génie électrique, génie électronique, génie de l’information ingénierie électronique capteurs
- sciences naturelles sciences chimiques chimie inorganique métalloïde
Vous devez vous identifier ou vous inscrire pour utiliser cette fonction
Programme(s)
Programmes de financement pluriannuels qui définissent les priorités de l’UE en matière de recherche et d’innovation.
Programmes de financement pluriannuels qui définissent les priorités de l’UE en matière de recherche et d’innovation.
Thème(s)
Les appels à propositions sont divisés en thèmes. Un thème définit un sujet ou un domaine spécifique dans le cadre duquel les candidats peuvent soumettre des propositions. La description d’un thème comprend sa portée spécifique et l’impact attendu du projet financé.
Données non disponibles
Les appels à propositions sont divisés en thèmes. Un thème définit un sujet ou un domaine spécifique dans le cadre duquel les candidats peuvent soumettre des propositions. La description d’un thème comprend sa portée spécifique et l’impact attendu du projet financé.
Appel à propositions
Procédure par laquelle les candidats sont invités à soumettre des propositions de projet en vue de bénéficier d’un financement de l’UE.
Données non disponibles
Procédure par laquelle les candidats sont invités à soumettre des propositions de projet en vue de bénéficier d’un financement de l’UE.
Régime de financement
Régime de financement (ou «type d’action») à l’intérieur d’un programme présentant des caractéristiques communes. Le régime de financement précise le champ d’application de ce qui est financé, le taux de remboursement, les critères d’évaluation spécifiques pour bénéficier du financement et les formes simplifiées de couverture des coûts, telles que les montants forfaitaires.
Régime de financement (ou «type d’action») à l’intérieur d’un programme présentant des caractéristiques communes. Le régime de financement précise le champ d’application de ce qui est financé, le taux de remboursement, les critères d’évaluation spécifiques pour bénéficier du financement et les formes simplifiées de couverture des coûts, telles que les montants forfaitaires.
Données non disponibles
Coordinateur
70174 Stuttgart
Allemagne
Les coûts totaux encourus par l’organisation concernée pour participer au projet, y compris les coûts directs et indirects. Ce montant est un sous-ensemble du budget global du projet.