Obiettivo
Passive microwave components were among the first practical devices fabricated from high-Tc superconductors. Compared to classical superconductors, however, high-Tc superconductors still yield several orders of magnitude higher residual losses, especially at elevated microwave field levels. SUPERMICA aims to identify the sources of these anomalously high microwave losses, minimise them using different fabrication techniques, and demonstrate an improved performance of standard and novel devices.
Several promising deposition techniques and structural and electromagnetic characterization methods have been used to improve the microstructure and reduce the microwave losses of YBa2Cu3O7-X films.
YBa2Cu3O7-X films of high structural quality have been epitaxially grown on single crystalline magnesium oxide and/or lanthanum aluminium oxide substrates using 4 deposition techniques. Transition temperatures between 85 K and 92 K, transition width of less than 1K, and critical current densities above 106 A cm{-2} at 77K have been measured inductively.
The surface impedance of these films has been measured at 87 GHz and 19 GHz. While there is only little scatter of the data for the surface resistance around 60 K and the penetration depth, the residual losses depend strongly on the oxygen content and order in the copper oxide chains and weakly on the cation stoichiometry.
The magnetic properties and the harmonic generation in field modulated microwave absorption of selected films have studied comparatively. The magnetoresistance, the irreversibility line and the harmonic generation depend on the film quality and thickness. Coplanar resonators have been patterned by photolithography from some of these films. Quality factors in excess of 40000 at 15 K and 8 GHz up to microwave fields of 104 A m{-1} have been achieved in the best case. However, at high fields there is a much stronger dependence on the film quality than at low fields.
APPROACH AND METHODS
At present, the most advanced techniques for the deposition of high quality epitaxial YBa2Cu3O7-X thin films onto small planar substrates are laser ablation and sputtering from stoichiometric targets, and chemical or physical co-evaporation from organometallic or metallic sources. Comparative studies on films produced by these techniques with systematically varied preparation conditions will be pursued to reveal trends between the observed structural and electromagnetic properties, with the aim of establishing causal relationships and learning to make an optimised material. Emphasis will be placed on reproducible deposition of high-quality films on substrates suitable for microwave devices. The crystallographic quality of the films will be characterised by X-ray diffraction, ion channelling, and for exceptionally good films, high-resolution transmission electron microscopy. The composition and topography of the film surface will be monitored by Rutherford backscattering, Auger electron spectroscopy and SE/ST microscopy. Electric and magneto-transport properties will also be studied, mainly in the superconducting but also in the normal conducting state. Emphasis will be given to DC magnetic studies to clarifying the correlation between high critical current densities due to impurity or defect-induced pinning, and low residual microwave losses requiring more homogeneous material. Both linear and non-linear microwave dissipation will be studied using calibrated surface impedance measurements and low magnetic field modulated microwave absorption. Patterned passive microwave devices will be produced from the best films. While coplanar resonators will serve for testing of film deposition and patterning techniques, more complex novel structures will be investigated for advanced signal processing.
POTENTIAL
SUPERMICA's work will lead to an improved understanding of the residual microwave losses of high-Tc superconducting films and their correlation with structural and surface imperfections, as well as of their current-carrying capability and magnetic properties. This will help develop the technology of making fully optimised YBa2Cu3O7-X films for microwave applications, eg in communication systems.
Campo scientifico (EuroSciVoc)
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
- scienze naturali scienze chimiche chimica inorganica metalli alcalino terrosi
- ingegneria e tecnologia ingegneria elettrica, ingegneria elettronica, ingegneria informatica ingegneria elettronica elaborazione del segnale
- scienze naturali scienze fisiche ottica microscopia electron microscopy
- ingegneria e tecnologia ingegneria dei materiali rivestimenti e pellicole
- scienze naturali scienze fisiche elettromagnetismo ed elettronica superconduttività
È necessario effettuare l’accesso o registrarsi per utilizzare questa funzione
Programma(i)
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Argomento(i)
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Dati non disponibili
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Invito a presentare proposte
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Dati non disponibili
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Meccanismo di finanziamento
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Dati non disponibili
Coordinatore
42097 WUPPERTAL
Germania
I costi totali sostenuti dall’organizzazione per partecipare al progetto, compresi i costi diretti e indiretti. Questo importo è un sottoinsieme del bilancio complessivo del progetto.