Ziel
New ceramic cell structures were realized by co-firing various two and/or three layer systems. These laminated multi layers were fabricated using a novel, ceramic powder filled thermoplastic (CPFT or Solufil (TM)). The development was divided into different sub tasks:
development of a self supporting two layer electrolyte system with electrical losses < 100 mV at 800 C and 300 mA/cm{2}.
development of an electrode (fuel or air) supported electrolyte structure.
development of an integrated PEN, consisting of a three layer, co-fired laminate structure of a thin state of the art electrolyte, supported by thicker electrodes on both sides.
The latter structure offers an attractive, cost effective fabrication process, because lamination is easy and process steps are minimized. Nevertheless, this integrated PEN structure implements a development process with high risks. In addition, for the technical application of this new ceramic cell structures special high temperature sealing materials were developed.
It was shown in the project that any of the powders, necessary for the preparation of SOFC components could be dispersed in Solufil (TM) and resulted in sintering shrinkage matched single layer SOFC components. Also, sintered double layer electrolytes of TZP/CSZ and GCO/CSZ were demonstrated as 5x5 cm{2} electrolytes, which were cell tested at 800 C. Cell performance around 0.2 W/cm{2} were demonstrated. The development of electrode supported thin electrolyte double-layers was demonstrated with the Solufil(TM) process. Small circular sample were sintered and cell tested. A performance of 0.15 W/cm{2} was observed for the cathode supported electrolyte at 800 C. Three-layer, co-fired cells were also manufactured. Due to residual mechanical stresses in the samples, no successful cell-test could be carried out. Tape-cast analogies of the Solufil(TM) samples yielded 0.3 W/cm{2}, showing the feasibility of the concept. For cell testing of the co-fired cell, a tailor made sealant, which resulted from the project, was used. This sealant was capable of forming hermetic seals to thick electrodes.
The proposed research is directed at developing ceramic cell structures (PEN : Positive/Electrolyte/ Negative),which will be fabricated by co-firing alaminate three-layer system made of a novel, ceramic-powder-filled thermoplast (CPFT).The proposed fabrication technique offers the possibility to minimize electrical losses in the PEN, by using thin electrolytes or by using alternative, highly conducting electrolyte materials, whereas co-firing of laminated PEN's is a novel fabrication procedure. The resulting PEN's will be used in SOFC reactors, which offers the economic benefit of low operation temperature (800 C).It is anticipated, that exploitation of the results will lead to lower system costs and longer life-times for SOFC systems.
The major research tasks are:
1. Basic CPFT experiments with one-layer SOFC components.
2. Sintering experiments with one layer SOFC components.
3. -Co-firing of two-layer electrolytes with high conduction.
4. Co-firing of two-layer electrode-supported electrolytes(PE or NE)
5 Co-firing of three-layer structures (integrated PEN)
The output of every task can result in an improved PEN structure, by conventionally adding the missing PEN element(s).Successful completion of task 3,4 and 5 offers the possibility of low temperature operation of an SOFC power plant, which gives a view on the required reduction of SOFC system costs in the order of 30%.
Wissenschaftliches Gebiet (EuroSciVoc)
CORDIS klassifiziert Projekte mit EuroSciVoc, einer mehrsprachigen Taxonomie der Wissenschaftsbereiche, durch einen halbautomatischen Prozess, der auf Verfahren der Verarbeitung natürlicher Sprache beruht. Siehe: Das European Science Vocabulary.
CORDIS klassifiziert Projekte mit EuroSciVoc, einer mehrsprachigen Taxonomie der Wissenschaftsbereiche, durch einen halbautomatischen Prozess, der auf Verfahren der Verarbeitung natürlicher Sprache beruht. Siehe: Das European Science Vocabulary.
Sie müssen sich anmelden oder registrieren, um diese Funktion zu nutzen
Programm/Programme
Mehrjährige Finanzierungsprogramme, in denen die Prioritäten der EU für Forschung und Innovation festgelegt sind.
Mehrjährige Finanzierungsprogramme, in denen die Prioritäten der EU für Forschung und Innovation festgelegt sind.
Thema/Themen
Aufforderungen zur Einreichung von Vorschlägen sind nach Themen gegliedert. Ein Thema definiert einen bestimmten Bereich oder ein Gebiet, zu dem Vorschläge eingereicht werden können. Die Beschreibung eines Themas umfasst seinen spezifischen Umfang und die erwarteten Auswirkungen des finanzierten Projekts.
Aufforderungen zur Einreichung von Vorschlägen sind nach Themen gegliedert. Ein Thema definiert einen bestimmten Bereich oder ein Gebiet, zu dem Vorschläge eingereicht werden können. Die Beschreibung eines Themas umfasst seinen spezifischen Umfang und die erwarteten Auswirkungen des finanzierten Projekts.
Aufforderung zur Vorschlagseinreichung
Verfahren zur Aufforderung zur Einreichung von Projektvorschlägen mit dem Ziel, eine EU-Finanzierung zu erhalten.
Daten nicht verfügbar
Verfahren zur Aufforderung zur Einreichung von Projektvorschlägen mit dem Ziel, eine EU-Finanzierung zu erhalten.
Finanzierungsplan
Finanzierungsregelung (oder „Art der Maßnahme“) innerhalb eines Programms mit gemeinsamen Merkmalen. Sieht folgendes vor: den Umfang der finanzierten Maßnahmen, den Erstattungssatz, spezifische Bewertungskriterien für die Finanzierung und die Verwendung vereinfachter Kostenformen wie Pauschalbeträge.
Finanzierungsregelung (oder „Art der Maßnahme“) innerhalb eines Programms mit gemeinsamen Merkmalen. Sieht folgendes vor: den Umfang der finanzierten Maßnahmen, den Erstattungssatz, spezifische Bewertungskriterien für die Finanzierung und die Verwendung vereinfachter Kostenformen wie Pauschalbeträge.
Koordinator
91050 München
Deutschland
Die Gesamtkosten, die dieser Organisation durch die Beteiligung am Projekt entstanden sind, einschließlich der direkten und indirekten Kosten. Dieser Betrag ist Teil des Gesamtbudgets des Projekts.