The future generation silicon-based devices require junction depths <100 nm. Dopant ions (B, BF2, As) will be implanted in Si at different temperatures, with energies <1 keV (for B) and of some keV (for BF2 and As). However, the successive annealing made for dopant activation produce non-equilibrium dopant diffusion, whose control needs deep knowledge of the microscopic mechanisms ruling this phenomenon.
To this end, the following experimental techniques will be used:
(i) secondary ion mass spectrometry SIMS) and spreading resistance profiling (SRP) to measure the annealing-induced chemical and electrical dopant redistribution, respectively, and;
(ii) medium energy ion scattering (MEIS), grazing incidence diffuse synchrotron X-ray scattering (GI-DXS) and transmission electron microscopy (TEM) for damage analysis. The final goal of the research will be the fabrication of an ultra-shallow junction device of high electrical performances.
The future generation silicon-based devices require junction depths <100 nm. Dopant ions (B, BF2, As) will be implanted in Si at different temperatures, with energies <1 keV (for B) and of some keV (for BF2 and As). However, the successive annealing made for dopant activation produce non-equilibrium dopant diffusion, whose control needs deep knowledge of the microscopic mechanisms ruling this phenomenon.
To this end, the following experimental techniques will be used:
(i) secondary ion mass spectrometry SIMS) and spreading resistance profiling (SRP) to measure the annealing-induced chemical and electrical dopant redistribution, respectively, and;
(ii) medium energy ion scattering (MEIS), grazing incidence diffuse synchrotron X-ray scattering (GI-DXS) and transmission electron microscopy (TEM) for damage analysis. The final goal of the research will be the fabrication of an ultra-shallow junction device of high electrical performances.
OBJECTIVES
The objectives of the research activity proposed here are:
1. The drawing of a comprehensive view of the atomic transport and electrical activation behaviour of dopants implanted in ultra-low energy regime. This will be possible by comparing and simulating the dopant profiles obtained by SIMS and SRP measurements before and after annealing;
2. The achievement of a complete characterisation of the damage introduced in a few 10 nm thick Si surface layers by implants at energies below 1 keV for B and of some keV for BF2 and As. This study will also be performed after annealing. The defect analyses will be determined by analysis and simulation of MEIS and synchrotron GI-DXS spectra, and by TEM imaging. The final goal will be the fabrication of a device with ultra-shallow junctions of high electrical performances.
DESCRIPTION OF WORK
Si wafers will be implanted at different temperatures with dopant ions (B, BF2, As) at energies <1 keV for B and of some keV for BF2 and As. Post-implant annealing will be done by rapid thermal processing (RTP) and spike annealing (SA).
The samples will be analysed by the following experimental techniques:
1. Electrical and chemical dopant profiling by SRP and a (unique in Europe) SIMS, respectively, with high depth resolution and sensitivity. The use of SRP is very important, because a high electrical activation is the basic requirement for the application of ultra-shallow doped layers in the future CMOS technology;
2. MEIS in double alignment mode has the unique capability of providing, also by spectra simulation, depth profiles of damage and of most implanted species with a resolution <1 nm;
3. GI-DXS at ESRF is a technique of surface diffraction particularly adequate to probe ultra-thin layers. Its most important feature is the ability to study atomic defect configurations in a size range from point defects to large clusters or extended defects. The high photon flux available at ID01 beamline makes these measurements possible with strong signal of the diffuse scattering. These measurements will be done before and after RTP and SA, and will be analysed also by codes of molecular static, e.g. the intensity patterns, calculated for given defect structures, will be compared with the experimental ones. Information on defect structure, depth distribution, size and concentration will then be obtained;
4. TEM observations: This technique will be very helpful to determine the onset of the transition from point-like defects to large clusters or extended defects, and to observe, by proper sample preparation, the two-dimensional delineation of shallow doped regions in devices. The 2D investigation is crucial to evaluate the lateral extension of the shallow junctions, which must be limited by the requirements of the future device technology.
Wissenschaftliches Gebiet (EuroSciVoc)
CORDIS klassifiziert Projekte mit EuroSciVoc, einer mehrsprachigen Taxonomie der Wissenschaftsbereiche, durch einen halbautomatischen Prozess, der auf Verfahren der Verarbeitung natürlicher Sprache beruht. Siehe: Das European Science Vocabulary.
CORDIS klassifiziert Projekte mit EuroSciVoc, einer mehrsprachigen Taxonomie der Wissenschaftsbereiche, durch einen halbautomatischen Prozess, der auf Verfahren der Verarbeitung natürlicher Sprache beruht. Siehe: Das European Science Vocabulary.
- Naturwissenschaften Naturwissenschaften Optik Mikroskopie electron microscopy
- Naturwissenschaften Naturwissenschaften Elektromagnetismus und Elektronik Halbleiterbauelement
- Naturwissenschaften Chemiewissenschaften analytische Chemie Massenspektrometrie
- Medizin- und Gesundheitswissenschaften Medizinische Biotechnologie Implantate
- Naturwissenschaften Naturwissenschaften theoretische Physik Teilchenphysik Photonen
Sie müssen sich anmelden oder registrieren, um diese Funktion zu nutzen
Programm/Programme
Mehrjährige Finanzierungsprogramme, in denen die Prioritäten der EU für Forschung und Innovation festgelegt sind.
Mehrjährige Finanzierungsprogramme, in denen die Prioritäten der EU für Forschung und Innovation festgelegt sind.
Thema/Themen
Aufforderungen zur Einreichung von Vorschlägen sind nach Themen gegliedert. Ein Thema definiert einen bestimmten Bereich oder ein Gebiet, zu dem Vorschläge eingereicht werden können. Die Beschreibung eines Themas umfasst seinen spezifischen Umfang und die erwarteten Auswirkungen des finanzierten Projekts.
Aufforderungen zur Einreichung von Vorschlägen sind nach Themen gegliedert. Ein Thema definiert einen bestimmten Bereich oder ein Gebiet, zu dem Vorschläge eingereicht werden können. Die Beschreibung eines Themas umfasst seinen spezifischen Umfang und die erwarteten Auswirkungen des finanzierten Projekts.
Aufforderung zur Vorschlagseinreichung
Verfahren zur Aufforderung zur Einreichung von Projektvorschlägen mit dem Ziel, eine EU-Finanzierung zu erhalten.
Daten nicht verfügbar
Verfahren zur Aufforderung zur Einreichung von Projektvorschlägen mit dem Ziel, eine EU-Finanzierung zu erhalten.
Finanzierungsplan
Finanzierungsregelung (oder „Art der Maßnahme“) innerhalb eines Programms mit gemeinsamen Merkmalen. Sieht folgendes vor: den Umfang der finanzierten Maßnahmen, den Erstattungssatz, spezifische Bewertungskriterien für die Finanzierung und die Verwendung vereinfachter Kostenformen wie Pauschalbeträge.
Finanzierungsregelung (oder „Art der Maßnahme“) innerhalb eines Programms mit gemeinsamen Merkmalen. Sieht folgendes vor: den Umfang der finanzierten Maßnahmen, den Erstattungssatz, spezifische Bewertungskriterien für die Finanzierung und die Verwendung vereinfachter Kostenformen wie Pauschalbeträge.
Koordinator
00185 ROMA
Italien
Die Gesamtkosten, die dieser Organisation durch die Beteiligung am Projekt entstanden sind, einschließlich der direkten und indirekten Kosten. Dieser Betrag ist Teil des Gesamtbudgets des Projekts.