Obiettivo
The aims are to develop a sound physical understanding of the process as applied to metallic and insulating compounds, and to exploit LAD for the preparation of a range of novel materials and multilayer structures for application in magnetics, microelectronics and X-ray optics.
Laser ablation deposition (LAD) has tremendous, but largely unrealised potential as a simple and versatile method of thin film preparation. This project aims to develop a sound physical understanding of the process as applied to metallic and insulating compounds, and to exploit LAD for the preparation of a range of novel materials and multilayer structures for application in magnetics, microelectronics and X-ray optics.
The nature and energy of the species evaporated in LAD, has been studied by use of CMA-QMS spectrometer. Particle filters for elimination of droplets ejected from the target during ablation have been developed. Epitaxial films have been grown of the yttrium cobalt(5) and yttrium nickel(5) compounds and layers of tungsten, niobium, yttrium and samarium. Diamond like carbon films exhibiting a long range crystalline order have been prepared. High quality epitaxial films of 1-2-3 superconductors have been prepared with yttrium, praseodymium and europium as well as bismuth strontium calcium copper oxide films doped with praseodymium and lithium. Off stoichiometric multilayers have been prepared of the bismuth superconductors interspaced with lead monoxide layers, with the aim of producing high critical temperature (Tc) superconductors without the need to perform annealing under lead vapour.
LAD is a rapidly developing method for thin film deposition which is particularly well suited for the preparation of compound thin films. Technical difficulties (high energies of evaporated species leading to interface mixing and resputtering and formation of droplets ejected from the target) have until now limited the development of LAD. A detailed assessment of LAD has been realised and a technique has been developed. In particular, a velocity selector to eliminate droplets has been designed and built. Also, 3 different types of model materials have been prepared, namely R2M17 intermetallic compounds, bismuth-based high critical temperature superconductors and diamond like carbon. Different types of materials have also been prepared to evaluate the versatility of the technique. The mechanisms involved in LAD have been examined experimentally and the laser target interactions have been modelled.
Studies on the nature of laser ablation have made a significant contribution to the understanding of the process. The laser ablation of metals has been clarified; just above the threshold for measurable ablation the removal rate is governed by the temperature dependence of the vapour pressure, and at higher fluence ablation via a laser produced plasma is the appropriate model. The highly energetic ions found in the plume are as consistent with the laser plasma ablation models. The much higher ablation rates found for ceramic materials can be understood in terms of the relatively long optical absorption depth leading to boiling of the directly heated region. The optical absorption processes leading to the production of ions in the plume are not yet determined, and deserve further investigation.
Laser ablation deposition (LAD) has tremendous, but largely unrealized potential as a simple and versatile method of thin film presentation. This project associates five groups with complementary experience in different aspects of LAD.
Campo scientifico (EuroSciVoc)
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
- scienze naturali scienze chimiche chimica inorganica metalli di transizione
- scienze naturali scienze chimiche chimica inorganica metalli alcalino terrosi
- scienze naturali scienze fisiche elettromagnetismo ed elettronica microelettronica
- scienze naturali scienze fisiche ottica fisica dei laser
- scienze naturali scienze fisiche elettromagnetismo ed elettronica superconduttività
È necessario effettuare l’accesso o registrarsi per utilizzare questa funzione
Programma(i)
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Argomento(i)
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Dati non disponibili
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Invito a presentare proposte
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Dati non disponibili
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Meccanismo di finanziamento
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Dati non disponibili
Coordinatore
38042 GRENOBLE
Francia
I costi totali sostenuti dall’organizzazione per partecipare al progetto, compresi i costi diretti e indiretti. Questo importo è un sottoinsieme del bilancio complessivo del progetto.