Obiettivo
We propose key experiments and theoretical calculations to better understand the nature of defects (trapping centres) in amorphous dielectrics: silicon oxide (SiO2) and nitride (Si3N4). This should help in solving the long-standing problem of the nature of traps in these compounds and give essential information on the role of Si-Si bonds as electrons or hole traps in SiO2. The results will be essential for many applications in solid-state physics an microelectronics. The localisation of carriers in Si3N4 is used in electrically erasable memory devices. The localisation of carriers generated by radiations in solids is widely used in radiation dosimetry.
Pioneering experimental works have suggested the possible Wigner cristallisation of trapped electrons or hole when the number of injected carriers is much weaker than the number of traps. A possible interpretation of the absence of Electron Paramagnetic Resonance in Si3N4 is the pairing of neighbouring localised carriers due to resonant exchange interactions. Experiments have been performed for only one density of localised carriers; they are insufficient to conclude definitively. We propose key experiments to probe this exciting interpretation: at low carrier densities the pairing between neighbours should disappear because exchange interactions are vanishingly small, the Wigner solid is expected to be paramagnetic and one should observe electron paramagnetic resonance. Hence we propose to investigate electron spin resonance at various densities of injected carriers. By increasing the density of injected carriers, we should observe a critical value at which the Wigner solid orders antiferromagnetically and the EPR line disappears. It is possible to vary the density of injected carriers by several orders of magnitude in Si-implanted SiO2 devices. We shall begin by this study. The more difficult experiment of varying the carrier density in Si3N4 will be carried out after.
If the Wigner cristallisation and antiferromagnetic order is confirmed, this should be the first evidence for a three-dimensional Wigner solid with significant exchange interactions.
It will then be useful to place it in the more general context of an almost localised system of identical fermions with exchange interactions. Some similarities should be found with another simpler systems of identical fermions: localised spin 1/2 3He nuclei.
For this reason, part of the project should contribute to answer remaining questions on antiferromagnetic ordering in solid 3He, a fascinating magnetic system that has suscitated a lot of experimental and theoretical works during the last two decades.
We plan to investigate experimentally the unexplored domain concerning the effect of strain on the ordered magnetic phases in bcc 3He. We will use precise sound-velocity and attenuation measurements.
We also propose an original approach for the description of the highly frustrated quantum states, using exact recursion relations that can be found on hierarchical Be the-like lattices that could be reasonable approximations to the real lattices for two-dimensional solid 3He films and three-dimensional bcc 3He.
The whole project could be an important contribution to the fundamental concept of exchange among almost-localised identical fermion formulated by Dirac a long time ago and leading to a generalised Heisenberg model, as observed in solid 3He.
Campo scientifico (EuroSciVoc)
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
Questo progetto non è ancora stato classificato con EuroSciVoc.
Suggerisci i campi scientifici che ritieni più rilevanti e aiutaci a migliorare il nostro servizio di classificazione.
È necessario effettuare l’accesso o registrarsi per utilizzare questa funzione
Programma(i)
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Argomento(i)
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Invito a presentare proposte
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Dati non disponibili
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Meccanismo di finanziamento
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Dati non disponibili
Coordinatore
91191 Gif-sur-Yvette
Francia
I costi totali sostenuti dall’organizzazione per partecipare al progetto, compresi i costi diretti e indiretti. Questo importo è un sottoinsieme del bilancio complessivo del progetto.