The aim of this project is to improve oxidation and corrosion resistanc e of non-oxide ceramics of the silicon nitride and related types, through systematic, basic research. Sintered silicon carbides of good oxidation resistance will be used as reference materials, and it would be expected that the final quality of the silicon nitrides will approach that of the silicon carbides. To provide guidelines for the direction of this basic study, and later to assist in the effective quantitative evaluation of material improvements, one potential application, metal forming dies, has been selected identifying a specific set of oxidation and corrosion conditions. This industrial application of non-oxide ceramics, and the silicon nitride based materials in particular, would appear to be ideally suited to their known high-temperature mechanical properties. The immediate economies to be achieved will result in large measure from the reductions in 'down-time' resulting from less frequent routine die replacement and premature die failure. The economic value of the increased basic understanding of the oxidation and corrosion behaviour of the silicon nitrides, and of the resulting improved oxidation and corrosion resistance, cannot be easily quantified. It is certain, however, to have a very significant impact on the future acceptance of these materials as substituents for metals in a wide range of high temperature applications.
Current theory suggests that the oxidation rate of materials that are highly resistance to oxidation is related to the type and amount of additives used during sintering.
The first route was to add yttrium oxide to silicon nitride via hot isostatic pressing (HIP). The weight change measured after oxidation in air at temperatures between 1400 1500 C showed a logarithmic kinetics. Passivation may be related to the high crystallinity of the oxide film formed on the surface of the ceramic.
The second route involved the use of an aluminium oxide-titanium oxide system as a densification aid to silicon nitride. This was chosen on the theoretical basis that both materials should be in thermodynamic equilibrium during the intergranular phase which should overcome the anticipated problem of intergranular phase cation release. The results of testing were encouraging. After oxidations carried out at 1300, 1400 and 1460 C, this material showed negligible weight gain.
The new, densified silicon nitride was used in the preparation of metallic die ceramic insert assemblies. These were then used in laboratory and factory environments to produce extrusion forged components for the rear axle of a truck. The configuration and strength of the metal die holder was inadequate to contain the elastic deformation of the ceramic liner caused by the hoop stresses created. During extrusion, there was severe adhesion of metal and metal oxide to the ceramic liner surface. Both problems may be controlled in both types of materials tested by the careful selection and control during the intergranular phase composition of the silicon nitride. A more complete solution may found in the development of special lubricant or fluxing systems. These would minimize the contact between the metal oxide and the non-oxide ceramic surface of the die.
SINTERED SILICON CARBIDES OF GOOD OXIDATION RESISTANCE WILL BE USED AS REFERENCE MATERIALS, AND IT WOULD BE EXPECTED THAT THE FINAL QUALITY OF THE SILICON NITRIDES WILL APPROACH THAT OF THE SILICON CARBIDES.
TO PROVIDE GUIDELINES FOR THE DIRECTION OF THIS BASIC STUDY, AND LATER TO ASSIST IN THE EFFECTIVE QUANTITATIVE EVALUATION OF MATERIALS'IMPROVEMENTS, ONE POTENTIAL APPLICATION, METAL FORMING DIES, HAS BEEN SELECTED, IDENTIFYING A SPECIFIC SET OF OXIDATION AND CORROSION CONDITIONS. THIS INDUSTRIAL APPLICATION OF NON-OXIDE CERAMICS, AND THE SILICON NITRIDE BASED MATERIALS IN PARTICULAR, WOULD APPEAR TO BE IDEALLY SUITED TO THEIR KNOWN HIGH-TEMPERATURE MECHANICAL PROPERTIES.
THE IMMEDIATE ECONOMIES TO BE ACHIEVED WILL RESULT IN LARGE MEASURE FROM THE REDUCTIONS IN "DOWN-TIME" RESULTING FROM LESS FREQUENT ROUTINE DIE REPLACEMENT AND PREMATURE DIE FAILURE.
THE ECONOMIC VALUE OF THE UNDERLYING INCREASED BASIC UNDERSTANDING OF THE OXIDATION AND CORROSION BEHAVIOUR OF THE SILICON NITRIDES, AND OF THE RESULTING IMPROVED OXIDATION AND CORROSION RESISTANCE CANNOT BE SO EASILY QUANTIFIED. IT IS CERTAIN, HOWEVER, TO HAVE A VERY SIGNIFICANT IMPACT ON THE FUTURE ACCEPTANCE OF THESE MATERIALS AS SUBSTITUENTS FOR METALS IN A WIDE RANGE OF HIGH TEMPERATURE APPLICATIONS.
Wissenschaftliches Gebiet (EuroSciVoc)
CORDIS klassifiziert Projekte mit EuroSciVoc, einer mehrsprachigen Taxonomie der Wissenschaftsbereiche, durch einen halbautomatischen Prozess, der auf Verfahren der Verarbeitung natürlicher Sprache beruht. Siehe: Das European Science Vocabulary.
CORDIS klassifiziert Projekte mit EuroSciVoc, einer mehrsprachigen Taxonomie der Wissenschaftsbereiche, durch einen halbautomatischen Prozess, der auf Verfahren der Verarbeitung natürlicher Sprache beruht. Siehe: Das European Science Vocabulary.
- Technik und Technologie Maschinenbau Tribologie Schmierung
- Naturwissenschaften Chemiewissenschaften anorganische Chemie anorganische Verbindungen
- Naturwissenschaften Chemiewissenschaften Elektrochemie Elektrolyse
- Naturwissenschaften Chemiewissenschaften anorganische Chemie Metalloide
- Technik und Technologie Werkstofftechnik Keramik
Sie müssen sich anmelden oder registrieren, um diese Funktion zu nutzen
Programm/Programme
Mehrjährige Finanzierungsprogramme, in denen die Prioritäten der EU für Forschung und Innovation festgelegt sind.
Mehrjährige Finanzierungsprogramme, in denen die Prioritäten der EU für Forschung und Innovation festgelegt sind.
Thema/Themen
Aufforderungen zur Einreichung von Vorschlägen sind nach Themen gegliedert. Ein Thema definiert einen bestimmten Bereich oder ein Gebiet, zu dem Vorschläge eingereicht werden können. Die Beschreibung eines Themas umfasst seinen spezifischen Umfang und die erwarteten Auswirkungen des finanzierten Projekts.
Daten nicht verfügbar
Aufforderungen zur Einreichung von Vorschlägen sind nach Themen gegliedert. Ein Thema definiert einen bestimmten Bereich oder ein Gebiet, zu dem Vorschläge eingereicht werden können. Die Beschreibung eines Themas umfasst seinen spezifischen Umfang und die erwarteten Auswirkungen des finanzierten Projekts.
Aufforderung zur Vorschlagseinreichung
Verfahren zur Aufforderung zur Einreichung von Projektvorschlägen mit dem Ziel, eine EU-Finanzierung zu erhalten.
Daten nicht verfügbar
Verfahren zur Aufforderung zur Einreichung von Projektvorschlägen mit dem Ziel, eine EU-Finanzierung zu erhalten.
Finanzierungsplan
Finanzierungsregelung (oder „Art der Maßnahme“) innerhalb eines Programms mit gemeinsamen Merkmalen. Sieht folgendes vor: den Umfang der finanzierten Maßnahmen, den Erstattungssatz, spezifische Bewertungskriterien für die Finanzierung und die Verwendung vereinfachter Kostenformen wie Pauschalbeträge.
Finanzierungsregelung (oder „Art der Maßnahme“) innerhalb eines Programms mit gemeinsamen Merkmalen. Sieht folgendes vor: den Umfang der finanzierten Maßnahmen, den Erstattungssatz, spezifische Bewertungskriterien für die Finanzierung und die Verwendung vereinfachter Kostenformen wie Pauschalbeträge.
Koordinator
20009 SAN SEBASTIAN
Spanien
Die Gesamtkosten, die dieser Organisation durch die Beteiligung am Projekt entstanden sind, einschließlich der direkten und indirekten Kosten. Dieser Betrag ist Teil des Gesamtbudgets des Projekts.