The exponential scaling down of silicon circuits obtained during the last decades is expected to continue for the next 15 years, leading eventually to random-access memories (DRAM) with a density of almost 20 Gbits per cm2. This will require fabrication of VLSI circuits with a minimum feature size of 100 nm. Below this critical size, even if fabrication at ~35 nm proves in the near future to be practical, the implementation of 64 Gbit and 256 Gbit DRAM generations is questionable mainly because of the scaling down of charge storage capacitors. As an alternative, the fabrication of new nanomemories should be investigated. The goal of this project is to fabricate a new Ge nano-crystals based memory which utilizes direct tunnelling and storage in the Ge islands. The advantage of the process is the use of Focused Ion Beam (FIB) nano-patterning of the substrate to precisely control (at the nm level) the islands size, shape and positioning. The exponential scaling down of silicon circuits obtained during the last decades is expected to continue for the next 15 years, leading eventually to random-access memories (DRAM) with a density of almost 20 Gbits per cm2. This will require fabrication of VLSI circuits with a minimum feature size of 100 nm. Below this critical size, even if fabrication at ~35 nm proves in the near future to be practical, the implementation of 64 Gbit and 256 Gbit DRAM generations is questionable mainly because of the scaling down of charge storage capacitors. As an alternative, the fabrication of new nanomemories should be investigated. The goal of this project is to fabricate a new Ge nano-crystals based memory which utilizes direct tunneling and storage in the Ge islands. The advantage of the process is the use of Focused Ion Beam (FIB) nano-patterning of the substrate to precisely control (at the nm level) the islands size, shape and positioning.
OBJECTIVES
The objective of the project is twofold : i) to develop and assess the potential for FIB nano-patterning for the microelectronics requirements in the sub 10 nm domain and ii) to demonstrate new generation of nano-crystals memories with potential mass fabrication and full compatibility with CMOS technology. These two goals that correspond to industrial challenges, will be achieved in collaboration with the two companies involved in this project. This collaboration will favor the tranfer of technology between research groups and industry trying to approach manufacturable devices. Combination of FIB nano-patterning and natural formation of Ge islands will permit to circumvent most of the problems induced by self-organisation (non reproducible device characteristics) with a fabrication process of device structures with minimum perturbation of the conventional MOS transistors technology.
DESCRIPTION OF WORK
The work will be divided in 5 major tasks:
1) nano-patterning of the substrate by Focused Ga+ Ions Beam at the nanometer scale. The aim of this task is to realise uniform array of sub-10 nm holes on large scale areas. The influence of the process parameters on the induced damage will be measured. Experimental conditions will be optimized to reduce the silicon surface degradation, lower the holes sizes and precisely control the holes shape and positioning;
2) restoring of the substrate by thermal annealing in ultra-high vacuum. Investigation will focus on the conditions for soft thermal annealing to guarantee total removal of crystalline defects and desorption of Ga implanted atoms without modifying the holes shape/size. At this step appearence of high index facets on the holes sides is expected. Facets angles will be varied by modifying the aspect ratios (height over lateral size) of the holes;
3) fabrication of an array of isolated Ge quantum dots (QD). Nucleation of Ge islands in the holes will be first investigated by in-situ STM in order to determine the experimental conditions of Volmer Weber growth (selective nucleation of islands). Growth process will then be transferred to MBE and LPCVD growth techniques. The characteristics of the Ge QDs arrays obtained by the different growth processes will be compared and analysed;
4) fabrication of the tunnel oxide (between the Ge islands) and of the control oxide. They will both be performed by in situ thermal oxidation to ensure a good quality oxide layer. The tunnel oxide fabrication is based on the different rates of oxidation of Ge and Si and on the oxide penetration from the edges of the islands to the Ge/Si interface. Ge/SiO2 demixion effects are also expected to occur in agreement with previous experimental results;
5) device memory fabrication and electrical characterization. The gate, source and drain regions of the MOSFET device will be fabricated using conventional 0.6 microns MOS process.
Campo scientifico (EuroSciVoc)
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
CORDIS classifica i progetti con EuroSciVoc, una tassonomia multilingue dei campi scientifici, attraverso un processo semi-automatico basato su tecniche NLP. Cfr.: Il Vocabolario Scientifico Europeo.
- scienze naturali scienze chimiche elettrochimica elettrolisi
- ingegneria e tecnologia nanotecnologia nanomateriali nanocristalli
- scienze naturali scienze fisiche elettromagnetismo ed elettronica microelettronica
- scienze naturali scienze chimiche chimica inorganica metalloidi
È necessario effettuare l’accesso o registrarsi per utilizzare questa funzione
Parole chiave
Parole chiave del progetto, indicate dal coordinatore del progetto. Da non confondere con la tassonomia EuroSciVoc (campo scientifico).
Parole chiave del progetto, indicate dal coordinatore del progetto. Da non confondere con la tassonomia EuroSciVoc (campo scientifico).
Programma(i)
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Programmi di finanziamento pluriennali che definiscono le priorità dell’UE in materia di ricerca e innovazione.
Argomento(i)
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Dati non disponibili
Gli inviti a presentare proposte sono suddivisi per argomenti. Un argomento definisce un’area o un tema specifico per il quale i candidati possono presentare proposte. La descrizione di un argomento comprende il suo ambito specifico e l’impatto previsto del progetto finanziato.
Invito a presentare proposte
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Dati non disponibili
Procedura per invitare i candidati a presentare proposte di progetti, con l’obiettivo di ricevere finanziamenti dall’UE.
Meccanismo di finanziamento
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Meccanismo di finanziamento (o «Tipo di azione») all’interno di un programma con caratteristiche comuni. Specifica: l’ambito di ciò che viene finanziato; il tasso di rimborso; i criteri di valutazione specifici per qualificarsi per il finanziamento; l’uso di forme semplificate di costi come gli importi forfettari.
Coordinatore
75794 PARIS CEDEX 16
Francia
I costi totali sostenuti dall’organizzazione per partecipare al progetto, compresi i costi diretti e indiretti. Questo importo è un sottoinsieme del bilancio complessivo del progetto.